Product Name | Chemical Composition | Yellowing | Hydrolysis resistance | Solid Content N.V.(%) |
Viscosity (CPS/25℃) |
100% Module (Kg/c㎡) |
Tensile Strength (Kg/c㎡) |
Elongation(%) | PH Value | Ion | Appearance | Characteristics |
JW-20SY | Polyether | Semi-yellowing | Hydrolysis bad | 20±1% | Below1000 | 15-25 | 200 ~ 500 | 1500 ~ 2500 | 7-9 | Anion | White emulsion | Waterborne PU soft bulking agent |
JWS-35NHR | Polyether | non-yellowing | Hydrolysis resistance | 35±1% | Below3000 | 30-40 | 200 ↑ | 1500↑ | 7-9 | Anion | White emulsion | Waterborne PU leather with a soft top skin |
JWS-3570NHR | Polyether | non-yellowing | Hydrolysis resistance | 35±1% | Below1500 | 60-80 | 250 ~ 650 | 500 ~ 900 | 7-9 | Anion | White emulsion | Waterborne PU leather with a Medium Hard Type top skin |
JW-120NHR | Polyether | non-yellowing | Hydrolysis bad | 30±1% | Below1000 | 15-25 | 200-500 | 1500 ~ 2500 | 7-8 | Non-ionic | White emulsion | Leather surface treatment and coating |
JW-40SY | Polyether | Semi-yellowing | Hydrolysis resistance | 35 ±1% | Below3000 | 20-30 | 300 ↑ | 1000↑ | 7-9 | Anion | White emulsion | split leather、synthetic leather post-lamination for sponge |
JWN-65A | Polyether | non-yellowing | Hydrolysis resistance | 35 ±1% | Below3000 | 15-25 | 250↑ | 1500↑ | 7-9 | Anion | Through blue color emulsion | Leather Adhesives |
JW-40S | Polyether | non-yellowing | Hydrolysis bad | 40 ±1% | Below3000 | 60-70 | 120↑ | 1500↑ | 7-9 | Anion | Milky Through blue color | Leather Adhesives |
JW-130SYR | Polyether | Semi-yellowing | Hydrolysis resistance | 30 ±1% | Below1000 | 15-25 | 200-500 | 1500 ~ 2500 | 7-9 | Anion | Through blue color emulsion | Nylon coated with water-based PU |
JWS-30NHR | Polyether | non-yellowing | Hydrolysis resistance | 35 ±1% | Below1500 | 30-40 | 200-500 | 1500 ~ 2500 | 7-9 | Anion | Through blue color emulsion | Nylon, denim spraying water-based PU |
JWB-230SY | Polyether | Semi-yellowing | Hydrolysis bad | 32 ±1% | Below1000 | 10↓ | 50↑ | 300↑ | 7-9 | Anion | White emulsion | Natural water-based PU leather post-lamination for sponge (PU/Acrylic copolymer) |
JW-25A-2 | Polyether/Polyester | non-yellowing | Hydrolysis resistance | 30 ±1% | Below1500 | 15-25 | 250-450 | 1000↑ | 6-8 | Anion | Milky Through blue color | Waterborne PU resin moisture permeable、water-resist top skin, Adhesives |
JW-3002 | Polyether/Polyester | non-yellowing | Hydrolysis resistance | 30 ±1% | Below300 | - | - | - | 6-8 | Non-ionic | clear | Waterborne PU soft elastic impregnated Shrink, wrinkle-free |
JW-30N | Polyether/Polyester | non-yellowing | Hydrolysis bad | 30 ±1% | Below300 | 10-15 | 200-300 | 420 ↑ | 7-9 | Non-ionic | White emulsion | Anti-pilling, increased color fastness |
JWS-5005K | Polyether | non-yellowing | Hydrolysis resistance | 50 ±1% | Below1500 | 5-15 | 200↑ | 1500↑ | 7-9 | Anion | Milky Through blue color | Soft top skin with water-based ink |
JWS-5010K | Polyether | non-yellowing | Hydrolysis resistance | 50 ±1% | Below1500 | 10-20 | 200↑ | 1500↑ | 7-9 | Anion | Milky Through blue color | Soft top skin with water-based ink |
JWB-5020K | Polyether/Polyester | non-yellowing | Hydrolysis resistance | 50 ±1% | Below1500 | 20-30 | 200↑ | 1500↑ | 7-9 | Anion | Milky Through blue color | Soft Adhesives with water-based ink |